MICROWAVE RADIATION INDUCED SYNTHESIS OF HYDROXYPROPYL METHYLCELLULOSE-GRAFT- (POLYVINYLALCOHAL-CO-ACRYLIC ACID) POLYMERIC NETWORK AND ITS IN VITRO EVALUATION.

Acta poloniae pharmaceutica · 2017 · Benefit · Low evidence

← Research stream

BenefitLow evidencePaper 6599

Study snapshot

PublicationActa poloniae pharmaceutica · 2017

Study typein_vitro

Reported directionBenefit

Evidence ratingLow

Abstract

A microwave induced irradiation synthesis, was proposed for the preparation of hydroxypropyl methylcellulose-graft-(polyvinylalcohal-co-acrylic acid) hydrogels. The hydrogels were separately synthesized by using microwave irradiation method and conventional water bath heating method. Moreover, the prepared hydrogels were loaded with an antihypertensive drug, captopril. Chemical groups, thermal stability and surface morphology of these hydrogels were characterized by FT-IR, DSC and SEM. Swelling ratios of the gels were measured gravimetrically at'pH 1.2 and 7.4. Results showed that micrographs obtained from scanning electron microscopy (SEM), revealed that gels synthesized using microwave irradiation had more uniformly porous network structures. The uniformity in porosity was due to rapid and instantaneous penetration of microwave energy throughout the surface and they had higher swelling ratios in comparison to hydrogels synthesized by water bath method. Thermal analysis (DCS and TGA) depicted that crosslinked polymers were more stable. FT-IR analysis had confirmed the formation of the new polymeric network. X-ray diffractogram revealed that crystallinity of HPMC was reduced in hydrogel prepared by microwave radiation. It had also been observed that high crosslinking density diminish swelling of hydrogel. A stable network of hydroxypropyl methylcellulose (HPMC), poly(vinylalcohal) (PVA) and acrylic acid was developed in shorter time period under influence of microwave radiations.

Machine Enhanced Logic

AI evidence extraction

Structured fields below were generated from the paper’s abstract and metadata to make the evidence easier to inspect. Automated extraction may be incomplete or incorrect; verify important details against the original paper.

Study typein_vitro

Effect directionbenefit

PopulationNot supplied

Sample sizeNot supplied

Exposuremicrowave

Evidence strengthLowConfidence: 74% · Peer reviewed: yes

Main findings

Hydrogels synthesized using microwave irradiation showed a more uniformly porous network structure and higher swelling ratios than hydrogels synthesized by conventional water bath heating. Thermal analysis indicated crosslinked polymers were more stable, FT-IR confirmed formation of a new polymeric network, and X-ray diffraction suggested reduced crystallinity of HPMC in microwave-prepared hydrogel; a stable network was developed in a shorter time under microwave radiation.

Outcomes measured

Hydrogel network morphology/porosity (SEM)
Swelling ratio at pH 1.2 and 7.4
Thermal stability (DSC/TGA)
Chemical group/network formation (FT-IR)
Crystallinity (X-ray diffractogram)

Limitations

Microwave exposure parameters (e.g., frequency, power, duration) not reported in the abstract
In vitro/materials study; no human or animal health outcomes reported
No sample size or replication details provided in the abstract

View raw extracted JSON

{
  "study_type": "in_vitro",
  "exposure": {
    "band": "microwave",
    "source": "laboratory microwave irradiation (polymer synthesis)",
    "frequency_mhz": null,
    "sar_wkg": null,
    "duration": null
  },
  "population": null,
  "sample_size": null,
  "outcomes": [
    "Hydrogel network morphology/porosity (SEM)",
    "Swelling ratio at pH 1.2 and 7.4",
    "Thermal stability (DSC/TGA)",
    "Chemical group/network formation (FT-IR)",
    "Crystallinity (X-ray diffractogram)"
  ],
  "main_findings": "Hydrogels synthesized using microwave irradiation showed a more uniformly porous network structure and higher swelling ratios than hydrogels synthesized by conventional water bath heating. Thermal analysis indicated crosslinked polymers were more stable, FT-IR confirmed formation of a new polymeric network, and X-ray diffraction suggested reduced crystallinity of HPMC in microwave-prepared hydrogel; a stable network was developed in a shorter time under microwave radiation.",
  "effect_direction": "benefit",
  "limitations": [
    "Microwave exposure parameters (e.g., frequency, power, duration) not reported in the abstract",
    "In vitro/materials study; no human or animal health outcomes reported",
    "No sample size or replication details provided in the abstract"
  ],
  "evidence_strength": "low",
  "confidence": 0.74,
  "peer_reviewed_likely": "yes",
  "keywords": [
    "microwave irradiation",
    "hydrogel",
    "hydroxypropyl methylcellulose",
    "polyvinyl alcohol",
    "acrylic acid",
    "captopril",
    "SEM",
    "FT-IR",
    "DSC",
    "TGA",
    "swelling ratio",
    "crystallinity"
  ],
  "suggested_hubs": []
}

AI can be wrong. Always verify against the paper.

AI-extracted fields are generated from the abstract and metadata and may be incomplete or incorrect. This material is for informational purposes and is not medical advice.

Identifiers and source

DOI: Not supplied
PubMed: 29624258

Read the original paper →

Related papers

← Back to the Research Library